Slide bearing comprising a primer system as adhesion promoter

ABSTRACT

A slide bearing can include a metal support, a primer layer, an adhesive layer applied directly thereto, and a sliding layer applied to the adhesive layer. The primer layer can include an oligomeric condensate of at least one silanol selected from the group having the formula: 
     
       
         
         
             
             
         
       
         
         
           
             wherein x is 1 or 2, y is 0 or 1.
 
The moieties R 1  and R 2  can be the same or different. The moieties R 1  and R 2  can be selected from the group consisting of methyl, ethyl, n-propyl, i-propyl, and a functionalized alkyl group R′—(CH 2 ) z —, wherein z is at least 1. Slide bearings comprising a primer system based on silanol oligomeric condensates show improved peel strength than their analogous slide bearings lacking the primer system.

CROSS-REFERENCE TO RELATED APPLICATION(S)

This application is a continuation of and claims priority under 35U.S.C. § 120 to U.S. patent application Ser. No. 13/931,010 entitled“SLIDE BEARING COMPRISING A PRIMER SYSTEM AS ADHESION PROMOTER,” by OlafSchmitjes, filed Jun. 28, 2013, which claims priority under 35 U.S.C. §119(e) to U.S. Patent Application No. 61/666,336 entitled “SLIDE BEARINGCOMPRISING A PRIMER SYSTEM AS ADHESION PROMOTER,” by Olaf Schmitjes,filed Jun. 29, 2012, both of which are assigned to the current assigneehereof and incorporated herein by reference in their entireties.

FIELD OF THE DISCLOSURE

The disclosure relates to a slide bearing comprising a metal support, aprimer layer, an adhesive layer, and a sliding layer. The primer layerincludes a silanol based oligomeric condensate.

BACKGROUND

Maintenance-free slide bearings which comprise a layer structure havinga metallic support material, an intermediate layer and a sliding layerapplied thereto have been known for a long time in a variety of formsfrom the prior art and are used in a wide variety of technical fields,for example in the field of automotive engineering.

EP 0 394 518 A1 describes a multilayer slide bearing material in whichthe metallic support material preferably consists of cold-rolled steelon which a layer of a copolymer of perfluoro(alkyl vinyl ether) andtetrafluoroethylene has been applied as intermediate layer. A slidinglayer composed of a PTFE compound material is in turn applied to theintermediate layer. In this slide bearing material, the intermediatelayer has the function of establishing firm adhesion of the slidinglayer to the support material. In order firstly to ensure adhesion ofthe intermediate layer to the support material, the surface of themetallic support material in this known slide bearing material has to bepretreated in a suitable manner by wet chemical means. The best resultsappear to be achieved by chromating of the surface of the metallicsupport. However, this process is problematical for a variety ofreasons, including environmental issues and others. As such, there is acontinued need for improved maintenance free slide bearings.

Therefore, it would be advantageous if a slide bearing could be producedthat would not require extensive pretreatment of the metal supportwithout sacrificing adhesive strength between the metal support and thesliding layer.

SUMMARY OF THE INVENTION

In a first embodiment, a slide bearing can include a metal support, aprimer layer, an adhesive layer applied directly thereto, and a slidinglayer applied to the adhesive layer. The primer layer can include anoligomeric condensate of at least one silanol selected from the grouphaving the formula:

-   -   wherein x is 1 or 2, y is 0 or 1.

The moieties R¹ and R² can be the same or different. The moieties R¹ andR² can be selected from the group consisting of methyl, ethyl, n-propyl,i-propyl, and a functionalized alkyl group R′—(CH₂)_(z)—, wherein z isat least 1. In embodiments, z can be 1, 2, 3, 4, or 5. In otherembodiments, z is not greater than 10, such as not greater than 8, notgreater than 7, not greater than 6, not greater than 5, not greater than4, or not greater than 3.

The adhesive layer can include perfluoroalkoxyethylene (PFA),tetrafluoroethylene-perfluoro(methyl vinyl ether) copolymer (MFA),ethylene tetrafluoroethylene (ETFE),tetrafluoroethylene-hexafluoropropylene (FEP), and any combinationthereof.

In another aspect, a method for producing a slide bearing includesapplying a primer liquid onto a metal support. The primer liquid caninclude at least one silanol or an oligomeric condensate of at least onesilanol. The silanol can be selected from the group having the formula

-   -   wherein x is 1 or 2, y is 0 or 1.        The moieties R¹ and R² can be the same or different. The        moieties R¹ and R² can be selected from the group consisting of        methyl, ethyl, n-propyl, i-propyl, and a functionalized alkyl        group R′—(CH₂)_(z)—, wherein z is at least 1. In embodiments, z        can be 1, 2, 3, 4, or 5. In other embodiments, z is not greater        than 10, such as not greater than 8, not greater than 7, not        greater than 6, not greater than 5, not greater than 4, or not        greater than 3.

The method can further include drying the primer liquid to form a primerlayer. The method can further include applying an adhesive precursoronto the primer layer to form an adhesive layer. Moreover, the methodcan include applying a sliding layer onto the adhesive layer.

BRIEF DESCRIPTION OF THE DRAWINGS

The present disclosure may be better understood, and its numerousfeatures and advantages made apparent to those skilled in the art byreferencing the accompanying drawings.

FIG. 1 shows an exemplary slide bearing in schematic sectional view; and

FIG. 2 shows a comparison graph of adhesive strength tests on slidebearings according to an embodiment.

The use of the same reference symbols in different drawings indicatessimilar or identical items.

DETAILED DESCRIPTION

In an embodiment, a slide bearing can include a metal support, a primerlayer, an adhesive layer applied directly thereto, and a sliding layerapplied to the adhesive layer, in which adhesion of the sliding layer tothe support material is ensured over the long term. Moreover the methodof forming the slide bearing can be without use of ecologicallyproblematical processes for surface pretreatment.

The structure of an exemplary slide bearing is shown in FIG. 1. Here,the metal support is denoted by 1, while 2 denotes the primer layer, 3denotes the adhesive layer and 4 denotes the sliding layer appliedthereto.

In an embodiment, the intermediate layer 3 comprises a primer layerwhich can include an oligomeric condensate of at least one silanol. Thesilanol features a polar moiety and a organic residue moiety. The polarmoiety that has an affinity to adhere to support materials, such asmetal support 1. Moreover the polar moiety of the silanol may condenseor oligomerize to form a network or a sheet which increases the adhesionto the metal support. The organic residue moiety has an affinity tointeract with the adhesive layer 3 depending from type, length, andphysical-chemical properties of the organic residue. For example, theorganic residue can interact with the adhesive layer throughvan-der-Waals forces, covalent bonds, or a combination thereof.

In embodiments the silanols that form primer layer 2 can be selectedfrom the group having the formula:

-   -   wherein x is 1 or 2, y is 0 or 1.

The moieties R¹ and R² can be the same or different. The moieties R¹ andR² can be selected from the group consisting of methyl, ethyl, n-propyl,i-propyl, and a functionalized alkyl group R′—(CH₂)_(z)—, wherein z isat least 1. In embodiments, z can be 1, 2, 3, 4, or 5. In otherembodiments, z is not greater than 10, such as not greater than 8, notgreater than 7, not greater than 6, not greater than 5, not greater than4, or not greater than 3.

In embodiments, R′ can be selected from the group consisting of vinyl,difluorovinyl, trifluoromethyl, pentafluoroethyl, heptafluoropropyl,nonafluorobutyl, undecafluoropentyl, tridecafluorohexyl,pentadecafluoroheptyl, heptadecafluorooctyl, methoxy, ethoxy,trifluoromethoxy, pentafluoroethoxy, heptafluoroproxy, nonafluorobutoxy,undecafluoropentoxy, tridecafluorohexanoyl, pentadecafluoroheptanoyl,heptadecafluorooctanoyl, dimethyl amino, diethlyamino,di(trifluoromethyl)amino, and di(pentafluoroethyl)amino.

In embodiments, the silanol can be selected from the group consistingof:

In other embodiments, two silanols can be mixed to form the primerlayer. The two silanol can be any two silanols of the aforementionedformulas. In yet further embodiments, two or more silanols can be mixedto form the primer layer.

Moreover, two silanols can be mixed in any weight ratio. For example,two silanols can be mixed in a weight ratio of at least about 1:1, suchas at least about 2:1, at least about 3:1, at least about 4:1, at leastabout 5:1, at leas about 10:1, at least about 20:1, or at least about50:1. Furthermore, it is contemplated to have any mixture of any twosilanols mixed with a third silanol in any weight ratio. Moreover, it iscontemplated to mix any two mixtures of two silanol to form a blend ofsilanols that form the primer layer.

In embodiments, the primer layer 2 has a thickness of at least about 0.2microns, such as at least about 0.5 micron, at least about 0.8 microns,at least about 1 micron, at least about 1.5 microns, at least about 2microns, at least about 2.5 microns, or at least about 3 microns. In yetother embodiments, the thickness is not greater than about 5 microns,such as not greater than about 4.5 microns, not greater than about 4microns, not greater than about 3.5 microns, not greater than about 3microns, not greater than about 2.5 microns, or not greater than about 2microns.

In yet further embodiments, the primer layer 2 and the adhesive layer 3can have a combined thickness of at least about 2 microns, such as atleast about 4 micron, at least about 6 microns, at least about 8microns, or at least about 10 microns.

The adhesive layer 3 comprises an adhesive layer comprising athermoplastic polymer or a blend of thermoplastic polymers. Thethermoplastic polymers can include perfluoroalkoxyethylene (PFA),tetrafluoroethylene-perfluoro(methyl vinyl ether) copolymer (MFA),ethylene tetrafluoroethylene (ETFE),tetrafluoroethylene-hexafluoropropylene (FEP), and any combinationthereof.

In an embodiment, the adhesive layer 3 can include a polymer blend ofthermoplastic polymers. The blend can include at least two thermoplasticfluoropolymers P1 and P2, wherein P1 is selected fromperfluoroalkoxyethylene (PFA) or tetrafluoroethylene-hexafluoropropylene(FEP). P2 is different from P1 and can be a polymer selected fromtetrafluoroethylene-hexafluoropropylene (FEP), modifiedtetrafluoroethylene-hexafluoropropylene (mFEP), perfluoroalkoxyethylene(PFA), modified perfluoroalkoxyethylene (mPFA), polyimide (PI),polyamidimide (PAI), polyphenylene sulfide (PPS), polyphenylene sulfone(PPSO2), liquid crystal polymers (LCP), polyether ether ketones (PEEK),aromatic polyesters (Ekonol), ethylene-tetrafluoroethylene (ETFE),tetrafluoro-ethylene-perfluoro (methyl vinyl ether) (MFA), modifiedpolytetrafluoroethylene (TFM), polyvinylidene fluoride (PVDF),ethylene-chlorotrifluoroethylene (ECTFE), polyethersulfone (PES), andpolyetherketone (PEK).

The blend of P1 and P2 can be in any a weight ratio. For example theweight ration of P1:P2 can be about 1:99, about 5:95, about 10:90, about15:85, about 20:80, about 25:75, about 30:70, about 35:65, about 40:60,about 45:55, or about 50:50.

In another embodiment, the adhesive layer 3 can comprise at least threefluoropolymers P1, P2, and P3, wherein P1 is perfluoroalkoxyethylene(PFA), P2 is tetrafluoroethylene-hexafluoropropylene (FEP). P3 isdifferent from P1 and P2. P3 can be a polymer selected from modifiedtetrafluoroethylene-hexafluoropropylene (mFEP), modifiedperfluoroalkoxyethylene (mPFA), polyimide (PI), polyamidimide (PAI),polyphenylene sulfide (PPS), polyphenylene sulfone (PPSO2), liquidcrystal polymers (LCP), polyether ether ketones (PEEK), aromaticpolyesters (Ekonol), ethylene-tetrafluoroethylene (ETFE),tetrafluoro-ethylene-perfluoro (methyl vinyl ether) (MFA), modifiedpolytetrafluoroethylene (TFM), polyvinylidene fluoride (PVDF),ethylene-chlorotrifluoroethylene (ECTFE), polyethersulfone (PES), andpolyetherketone (PEK).

In embodiments, each of the polymer of the adhesive layer 3 can bepresent at various weight percentages. For example, P1 can comprise atleast about 1 wt %, at least about 2 wt %, at least about 5 wt %, atleast about 10 wt %, at least about 20 wt %, at least about 30 wt %, atleast about 40 wt %, or at least about 50 wt % of the adhesive layer. Inother embodiments, P2 can comprise at least about 1 wt %, at least about2 wt %, at least about 5 wt %, at least about 10 wt %, at least about 20wt %, at least about 30 wt %, at least about 40 wt %, or at least about50 wt % of the adhesive layer. In yet other embodiments, P3 or anysubsequent polymer can comprise can comprise at least about 1 wt %, atleast about 2 wt %, at least about 5 wt %, at least about 10 wt %, atleast about 20 wt %, at least about 30 wt %, at least about 40 wt %, atleast about 50 wt %, at least about 60 wt %, at least about 70 wt %, atleast about 80 wt %, at least about 90 wt %, or at least about 95 wt %of the adhesive layer.

In yet other embodiments, some polymers of the blend for the adhesivelayer 3 do not exceed certain weight percentages. For example, theweight percentage of P1 is not greater than about 50 wt %, not greaterthan about 40 wt %, not greater than about 30 wt %, not greater thanabout 20 wt %, not greater than about 10 wt %, not greater than about 5wt %, not greater than about 2 wt %, not greater than about 1 wt % ofthe adhesive layer. In other embodiments, the weight percentage of P2 isnot greater than about 50 wt %, not greater than about 40 wt %, notgreater than about 30 wt %, not greater than about 20 wt %, not greaterthan about 10 wt %, not greater than about 5 wt %, not greater thanabout 2 wt %, not greater than about 1 wt % of the adhesive layer. Inyet other embodiments, the weight percentage of P3 or any subsequentpolymer is not greater than about 95 wt %, not greater than about 90 wt%, not greater than about 80 wt %, not greater than about 70 wt %, notgreater than about 60 wt %, not greater than about 50 wt %, not greaterthan about 40 wt %, not greater than about 30 wt %, not greater thanabout 20 wt %, not greater than about 10 wt %, not greater than about 5wt %, not greater than about 2 wt %, or not greater than about 1 wt % ofthe adhesive layer.

Variation of the ratio of polymers P1, P2 and P3 provides for changes inthe MFI (melt flow index), as specified by DIN EN ISO 1133, which isincorporated herein in its entirety. The MFI is determined by the massof polymer that can extrude through an orifice of defined dimensions ata specified temperature and load within 10 minutes. In general, the loadis 5 kg and the temperature is approximately the melting point of thematerial to be characterized. For example, PFA has a melting point ofapproximately 372° C. and FEP or ETFE have melting points ofapproximately 297° C.

In embodiments, the MFI of the adhesive can be from 1 to 100 g/10 min,such as from 2 to 50 g/10 min, or from 3 to 25 g/10 min.

The sliding layer 4 applied to the adhesive layer 3 can be a PTFEcompound tape, in particular as a surface-pretreated, preferably etched,PTFE compound tape. The PTFE compound layer 4 used can contain variousfillers to improve the mechanical properties, e.g. fibers, inorganicmaterials, thermoplastic materials, or mineral materials, or mixturesthereof. Examples of fibers can include glass fibers, carbon fibers, andaramids. Examples of inorganic materials can include ceramic materials,carbon, glass, graphite, aluminum oxide, molybdenum sulfide, tungstendisulfide, bronze, and silicon carbide. The inorganic materials can bein the form of woven fabrics, powders, spheres, or fibers. Examples ofthermoplastic materials can include polyimide (PI), polyamidimide (PAI),polyphenylene sulfide (PPS), polyphenylene sulfone (PPSO2), liquidcrystal polymers (LCP), polyether ether ketones (PEEK), polyethersulfone(PES), polyetherketone (PEK), and aromatic polyesters (Ekonol). Examplesof mineral materials can include wollastonite and barium sulfate.

In other embodiments, the sliding layer includes PTFE, polyamide (PA),polyimide (PI), polyether ether ketone (PEEK), or a mixture thereof. Inone embodiment, the sliding layer is perforated, air-permeable, or both.

In a further embodiment, the sliding layer 4 has a thickness of at leastabout 0.01 mm, such as at least about 0.05 mm, at least about 0.1 mm, orat least about 0.2 mm. In other embodiments, the sliding layer 4 has athickness of not greater than about 2.0 mm, such as not greater thanabout 1.5 mm, not greater than about 1.0 mm, not greater than about 0.8mm, not greater than about 0.5 mm, not greater than about 0.4 mm, or notgreater than about 0.35 mm. In other embodiments, the sliding layer 4has a thickness in a range from about 0.2 mm to about 0.4 mm, such asfrom about 0.2 mm to about 0.25 mm and from about 0.28 mm to about 0.32mm. In one particular embodiment, the sliding layer has a thickness hasa thickness of about 0.24 mm. In another particular embodiment, thesliding layer has a thickness has a thickness of about 0.30 mm.

In embodiments, where the sliding is made of various polymers, suchsliding layer can further comprise at least one filler selected fromfibers, glass fibers, carbon fibers, aramids, inorganic materials,ceramic materials, carbon, glass, graphite, aluminum oxide, molybdenumsulfide, tungsten disulfide, bronze, silicon carbide, woven fabrics,powders, spheres or fibers, thermoplastic materials, in particularpolyimide (PI), polyamidimide (PAI), polyphenylene sulfide (PPS),polyphenylene sulfone (PPSO2), liquid crystal polymers (LCP), polyetherether ketones (PEEK), aromatic polyesters (Ekonol), mineral materials,wollastonite, barium sulfate, or mixtures thereof. The filler can be ina proportion from about 1 to about 40% by volume, from about 5 to about30% by volume, from about 10 to about 20% by volume.

In an embodiment, the slide bearing can be characterized by improvedadhesion of the sliding layer 4 to the support material 1 brought aboutby the adhesive layer 3 and the primer layer 2. FIG. 2 displays thebonding strength of a sliding layer in the presence and absence of theprimer layer 2.

Owing to the improved adhesion to even an unpretreated surface of themetal support, in particular to cold-rolled steel, cold-rolled andsubsequently electrolytically zinc-plated steel, aluminum, or stainlesssteel, ecologically problematical and disposal-intensive wet chemicalpretreatment processes, in particular chromating, can be dispensed with.

Physical processes for surface pretreatment of the adhesive (e.g. plasmapretreatment by corona discharge) as are described, for example, in EP 0848 031 B1 in which a functionalized thermoplastic fluoropolymer islikewise described as constituent of a laminate, are no longernecessary, as studies carried out by the applicant have shown. Theprocess for producing the slide bearing can therefore be carried out atsignificantly lower costs and with less ecological impact compared tothe prior art.

The metal support can be of any structure or shape. In embodiments, themetal support can be a plate, a sheet, a woven fabric, a mesh, or metalfoam. In embodiments, the metal support includes steel, cold-rolledsteel material No. 1.0338, cold-rolled steel material No. 1.0347, mattzinc-plated steel, stainless steel material No. 1.4512, stainless steelmaterial No. 1.4720, stainless steel material No. 1.4310, aluminum,alloys, or any combinations thereof.

In other embodiments, the metal support can have a coating. The coatingcan be a layer of another metal or alloy. In embodiments, the coating isa metal or alloy containing at least one of the following metals:chromium, molybdenum, tungsten, manganese, iron, ruthenium, osmium,cobalt, rhodium, iridium, nickel, palladium, platinum, copper, silver,gold, zinc, cadmium, mercury, aluminum, gallium, indium, thallium,silicon, germanium, tin, lead, antimony, and bismuth.

In yet other embodiments, the coating can be a copper alloy, acopper-tin alloy, a copper-zinc alloy, a bronze, a phosphor bronze, asilicon bronze, a brass, or any combinations thereof.

In an embodiment, the metal support used in the slide bearing can have asurface of a varying nature. Owing to the improved adhesion propertiesof the adhesive layer with the primer system, the metal support can haveeither a smooth surface or a roughened or structured surface (forexample, as achieved by brushing, sandblasting, embossing of astructure). Regardless of the surface roughness, the surface can also bemodified to form a plated surface, such as an electrolyticallyzinc-plated surface.

The thickness of the adhesive layer can correspond essentially to theroughness of the metal support, defined as the distance R_(max) betweenthe maximum profile peak height and the maximum profile valley depth ofthe roughness profile of the surface of the metal support. In this way,it can be ensured that a sufficiently thick adhesive layer is applied tothe metal support so that a full-area adhesive bond between slidinglayer and metal support is ensured. The adhesive layer should also notbe made too thick. In this case, there would be a risk that, on joiningthe layers, parts of the adhesive layer could be pressed out from theadhesive bond or cohesive rupture could occur within parts of theadhesive layer projecting above the roughness profile of the metalsupport surface when the slide bearing is subjected to shear stress. Forexample, the thickness can be at least about 1 micron, such as at leastabout 2 microns, at least about 3 microns, at least about 5 microns, atleast about 10 microns, at least about 15 microns, or at least about 35microns. In other embodiments, the thickness can be not greater thanabout 40 microns, such as not greater than about 35 microns, not greaterthan about 30 microns, not greater than about 25 microns, not greaterthan about 20 microns, not greater than about 15 microns, or not greaterthan about 10 microns.

The metal support can have an average surface roughness R_(a) of lessthan about 400 microns, less than about 200 microns, less than about 100microns, less than about 50 microns, less than about 25 microns, lessthan about 20 microns, less than about 15 microns, less than about 10microns, less than about 5 microns, less than about 3 microns, less thanabout 2 microns, less than about 1 micron.

The slide bearing according to any one of the preceding claims, whereinthe metal support has an average surface roughness R_(a) of at leastabout 0.01 micron, at least about 0.02 micron, at least about 0.05micron, at least about 0.1 micron, at least about 0.5 micron, at leastabout 1 micron, at least about 2 microns, at least about 5 microns, atleast about 10 microns, at least about 20 microns, at least about 50microns, at least about 100 microns, at least about 200 microns, atleast about 500 microns.

In yet another embodiment, the metal support can have an average surfaceroughness R_(a) in the range from about 0.1 micron to about 400 microns,from about 0.5 micron to about 100 microns, or from about 1 micron toabout 50 microns.

To improve the mechanical and general physical properties of the slidebearing, the adhesive layer 3 can contain fillers. Fillers can increaseand/or improve the thermal conductivity and/or the wear properties.Fillers can be fibers, inorganic materials, thermoplastic materials,mineral materials, or mixtures thereof. For example, fibers can includeglass fibers, carbon fibers, and aramids. Inorganic materials caninclude ceramic materials, carbon, glass, graphite, aluminum oxide,molybdenum sulfide, tungsten disulphide, bronze, and silicon carbide.The inorganic materials can be in the form of woven fabrics, powders,spheres or fibers. Examples of thermoplastic materials can includepolyimide (PI), polyamidimide (PAI), polyphenylene sulfide (PPS),polyphenylene sulfone (PPSO2), liquid crystal polymers (LCP), polyetherether ketones (PEEK), polyethersulfone (PES), polyetherketone (PEK), andaromatic polyesters (Ekonol). Example of mineral materials can includewollastonite and barium sulfate.

The proportion of filler in the adhesive layer 3 can be from about 1 toabout 40% by volume, such as from about 5 to about 30% by volume, fromabout 10 to about 25% by volume, or even from about 20 to about 25% byvolume. The thickness of the intermediate layer 3 can be in the rangefrom about 0.001 mm to 0.4 mm, such as from 0.01 to 0.05 mm.

In an embodiment, a method of producing a slide bearing includesapplying a primer liquid onto a metal support. The primer liquid caninclude at least one silanol or an oligomeric condensate of at least onesilanol. The silanol can be selected from the group having the formula

-   -   wherein x is 1 or 2, y is 0 or 1.        The moieties R¹ and R² can be the same or different. The        moieties R¹ and R² can be selected from the group consisting of        methyl, ethyl, n-propyl, i-propyl, and a functionalized alkyl        group R′—(CH₂)_(z)—, wherein z is at least 1. In embodiments, z        can be 1, 2, 3, 4, or 5. In other embodiments, z is not greater        than 10, such as not greater than 8, not greater than 7, not        greater than 6, not greater than 5, not greater than 4, or not        greater than 3.

The method can further include drying the primer liquid to form a primerlayer. The method can further include applying an adhesive precursoronto the primer layer to form an adhesive layer. Moreover, the methodcan include applying a sliding layer onto the adhesive layer.

In embodiments, applying of the primer liquid can include spraying,brushing, and dip coating. The primer liquid can include an organicsolvent, water, or a combination thereof. In embodiments, the organicsolvent can be methanol, ethanol, propanol, iso-propanol, butanol,diethyl ether, tetrathydrofuran, acetone, ethyl acetate, or anycombination thereof.

The adhesive precursor can be in the form of a film, a foil, a powder,or any combination thereof. The adhesive is thereby generated uponthermal treatment, e.g., during the lamination process when the slidinglayer is applied onto the metal support.

In embodiments, the sliding layer can be applied by laminating, bycoiling, by paste spreading, or any combination thereof. For pastespreading, a sliding precursor in form of a paste or high viscous slurryis applied onto the adhesive or the adhesive precursor followed by adrying, calendar, or curing step, which result in the sliding layerlaminated onto the metal support.

In another embodiment, a filler of the group of filler listed above canbe added to the sliding layer precursor or the adhesive precursor.

In one embodiment, both the metal support and the sliding layer are ineach case rolled off a roll as continuous material. Primer liquid isapplied to the metal support followed by adhesive precursor. The layersare joined to one another under pressure and at elevated temperature ina laminating roller apparatus. To achieve further-improved adhesion ofthe adhesive layer to the metal support together with improved corrosionproperties of the metal support, an embodiment of the process providesfor the surface of the metal support to be roughed and/orsurface-upgraded. In other embodiments, the method can include coatingthe metal surface.

The surface of the metal support can be treated by electrolyticzinc-plating to roughen, upgrade, or coat the surface. This is donebefore application of the adhesive layer. In other embodiments, thesurface area of the metal support can be increased by mechanicalstructuring. The structuring can include brush-finishing, sand-blasting,etching, perforating, pickling, punching, pressing, curling, deepdrawing, decambering, incremental sheet forming, ironing, laser cutting,rolling, hammering, embossing, undercutting, and any combinationsthereof. For example, embossing of a structure, allows for thepossibility of intermeshing, which has a positive effect on theresulting bonding forces.

In another embodiment, the surface of the metal support can bedegreased. Degreasing can be done by a washing process with a soapsolution and/or rinsing with an organic solvent. Solvents for thedegreasing process can be acetone, ethanol, isopropyl alcohol, or anycombination thereof. Alternatively, an ammonia solution, such as a 0.5%ammonia solution can be used.

In an embodiment, the improved adhesive strength can be determined bymeans of a 180° peel test using sandwich laminates.

EXAMPLES

180°-T-Peel-Test

The 180°-T-peel test is described in DIN EN 1895, which is incorporatedherein in its entirety. Strips of specimens having a five-layerstructure are prepared. The layer set-up is: Steel backing, adhesive,sliding layer, adhesive, steel backing. The strips have a width of 25mm. Clamps are affixed at one end to the opposing steel lips. The steelbackings are pulled apart and the peel force for separating the steelbackings is measured.

In one experiment, strips are prepared having ETFE as material for theadhesive layer. Cold-rolled steel of the grade 1.0338 is selected asmetallic backing and a PTFE compound tape having a filler content of 25%is selected as sliding layer. In one experiment the metallic backing istreated with a primer liquid to form a primer layer from anaminopropylsilanol-condensate.

As the experimental results presented in FIG. 2 show, in the absence ofthe primer, the bonding strength was measured to be 50 N/in. In thepresence the bonding strength almost tripled to about 140 N/in.

Slide bearings can be prepared in a vast number of very different shapesand sizes. The smallest bearing, also called a pico bearing, is only afew μm in height compared to bearings for other applications that couldbe up to 500 mm.

Slide Bearings can include plane bearings, annular bearings, bushings,balljoint bearings (half spheres), plain bearings, axial bearings,thrust bearings, linear bearings, bearing shells, bearing cups andcombinations thereof.

It is advantageous that the bearing is maintenance free. The term“maintenance-free” describes bearings that do not need to be greased aswas the case for bearings in early car doors. Yet, the life time ofmaintenance-free bearings exceeds the average life time of the productthese bearings are incorporated or the life time of conventionalbearings applied for the same purpose.

Slide bearings are applied in a broad spectrum of commercial industryranging from the heavy metal industry to the automotive and bikeindustry, even into baking industry, laptop/mobile phone hinges,bearings for solar applications and more

Note that not all of the activities described above in the generaldescription or the examples are required, that a portion of a specificactivity may not be required, and that one or more further activitiesmay be performed in addition to those described. Still further, theorder in which activities are listed are not necessarily the order inwhich they are performed.

In the foregoing specification, the concepts have been described withreference to specific embodiments. However, one of ordinary skill in theart appreciates that various modifications and changes can be madewithout departing from the scope of the invention as set forth in theclaims below. Accordingly, the specification and figures are to beregarded in an illustrative rather than a restrictive sense, and allsuch modifications are intended to be included within the scope ofinvention.

As used herein, the terms “comprises,” “comprising,” “includes,”“including,” “has,” “having” or any other variation thereof, areintended to cover a non-exclusive inclusion. For example, a process,method, article, or apparatus that comprises a list of features is notnecessarily limited only to those features but may include otherfeatures not expressly listed or inherent to such process, method,article, or apparatus. Further, unless expressly stated to the contrary,“or” refers to an inclusive-or and not to an exclusive-or. For example,a condition A or B is satisfied by any one of the following: A is true(or present) and B is false (or not present), A is false (or notpresent) and B is true (or present), and both A and B are true (orpresent).

Also, the use of “a” or “an” are employed to describe elements andcomponents described herein. This is done merely for convenience and togive a general sense of the scope of the invention. This descriptionshould be read to include one or at least one and the singular alsoincludes the plural unless it is obvious that it is meant otherwise.

Benefits, other advantages, and solutions to problems have beendescribed above with regard to specific embodiments. However, thebenefits, advantages, solutions to problems, and any feature(s) that maycause any benefit, advantage, or solution to occur or become morepronounced are not to be construed as a critical, required, or essentialfeature of any or all the claims.

After reading the specification, skilled artisans will appreciate thatcertain features are, for clarity, described herein in the context ofseparate embodiments, may also be provided in combination in a singleembodiment. Conversely, various features that are, for brevity,described in the context of a single embodiment, may also be providedseparately or in any subcombination. Further, references to valuesstated in ranges include each and every value within that range.

What is claimed is:
 1. A slide bearing comprising, a metal support; aprimer layer, wherein the primer layer consists of at least one silanol,an oligomeric condensate of at least one silanol, or combinationthereof, wherein the at least one silanol is selected from the grouphaving the formula

wherein x is 1 or 2, y is 0 or 1, wherein R¹ and R² are the same ordifferent and are selected from the group consisting of methyl, ethyl,n-propyl, i-propyl, and a functionalized alkyl group R′—(CH₂)_(z),wherein z is at least 1; an adhesive layer applied directly to theprimer layer, wherein the adhesive layer is selected from the groupconsisting of perfluoroalkoxyethylene (PFA),tetrafluoroethylene-perfluoro(methyl vinyl ether) copolymer (MFA),ethylene tetrafluoroethylene (ETFE),tetrafluoroethylene-hexafluoropropylene (FEP), and any combinationthereof; and a sliding layer.
 2. The slide bearing according to claim 1,wherein R′ is selected from the group consisting of vinyl,difluorovinyl, trifluoromethyl, pentafluoroethyl, methoxy, ethoxy,trifluoromethoxy, pentafluoroethoxy, dimethyl amino, diethlyamino,di(trifluoromethyl)amino, and di(pentafluoroethyl)amino.
 3. The slidebearing according to claim 1, wherein two silanols are selected in aweight ratio of at least about 1:1.
 4. The slide bearing according toclaim 1, wherein the primer layer has a thickness of at least about 0.2microns.
 5. The slide bearing according to claim 4, wherein thethickness is not greater than about 5 microns.
 6. The slide bearingaccording to claim 1, wherein the primer layer and the adhesive layerhave a combined thickness of at least about 2 microns.
 7. The slidebearing according to claim 1, wherein the primer layer and the adhesivelayer have a combined bonding strength after T-peel force according toDIN EN 1895 of at least about 100 N/cm.
 8. The slide bearing to claim 1,wherein the primer layer, the adhesive layer and the sliding layer havea combined bonding strength after T-peel force according to DIN EN 1895of at least about 70 N/cm.
 9. The slide bearing according to claim 1,wherein the sliding layer comprises polytetrafluoroethylene, polyamide,polyimide, polyether ether ketone, or a mixture thereof.
 10. The slidebearing according to claim 1, wherein the sliding layer comprises atleast one filler.
 11. The slide bearing according to claim 10, whereinthe at least one filler comprises fiber, glass fiber, carbon fiber,aramid, inorganic material, ceramic material, carbon, glass, graphite,aluminum oxide, molybdenum sulfide, tungsten disulfide, bronze, siliconcarbide, woven fabric, powder, sphere, thermoplastic material, polyimide(PI), polyamidimide (PAI), polyphenylene sulfide (PPS), polyphenylenesulfone (PPSO2), liquid crystal polymer (LCP), polyether ether ketone(PEEK), aromatic polyester (Ekonol), mineral material, wollastonite,barium sulfate, or any combination thereof.
 12. The slide bearingaccording to claim 1, wherein the metal support comprises steel,cold-rolled steel, material No. 1.0338 or 1.0347, matt zinc-platedsteel, stainless steel, material No. 1.4512 or 1.4720, aluminum, bronze,alloys, or any combination thereof.